Method for coating a substrate surface and coated product

ABSTRACT

The present invention provides a cold sprayed layer of tungsten, molybdenum, titanium, zirconium, or of mixtures of two or more of tungsten, molybdenum, titanium and zirconium, or of alloys of two or more of tungsten, molybdenum, titanium and zirconium, or of alloys of tungsten, molybdenum, titanium, zirconium with other metals, wherein the cold spayed layer has an oxygen content of below 1,000 ppm.

CROSS REFERENCE TO PRIOR APPLICATIONS

This application is a divisional of U.S. application Ser. No. 11/913,579, filed on Sep. 18, 2009. U.S. application Ser. No. 11/913,579 is a U.S. National Phase application under 35 U.S.C. §371 of International Application No. PCT/EP2006/003967, filed on Apr. 28, 2006, which claims benefit to U.S. Provisional Application No. 60/678,057, filed on May 5, 2005. The International Application was published in English on Nov. 9, 2006 as WO 2006/117144 A1 under PCT Article 21(2).

FIELD

The present invention relates to a method of applying coatings which contain only small amounts of gaseous impurities, in particular oxygen.

BACKGROUND

The application of refractory metal coatings to surfaces exhibits numerous problems.

In conventional processes, the metal is completely or partially melted in most cases, as a result of which the metals readily oxidise or absorb other gaseous impurities. For this reason, conventional processes such as deposition-welding and plasma spraying must be carried out under a protecting gas or in vacuo.

In such cases, the outlay in terms of apparatus is high, the size of the components is limited, and the content of gaseous impurities is still unsatisfactory.

The pronounced introduction of heat transmitted into the object to be coated leads to a very high potential for distortion and means that these processes cannot be employed in the case of complex components, which often also contain constituents that melt at low temperatures. Complex components must therefore be taken apart before they are re-processed, with the result, in general, that re-processing is scarcely economical and only recycling of the material of the components (scrapping) is carried out.

Moreover, in the case of vacuum plasma spraying, tungsten and copper impurities, which originate from the electrodes used, are introduced into the coating, which is generally undesirable. In the case of, for example, the use of tantalum or niobium coatings for corrosion protection, such impurities reduce the protective effect of the coating by the formation of so-called micro-galvanic cells.

Moreover, such processes are processes of melt metallurgy, which always involve the inherent disadvantages thereof, such as, for example, unidirectional grain growth. This occurs in particular in laser processes, where a suitable powder is applied to the surface and melted by means of a laser beam. A further problem is the porosity, which can be observed in particular when a metal powder is first applied and is subsequently melted by means of a heat source. Attempts have been made in WO 02/064287 to solve these problems by merely melting on the powder particles by means of an energy beam, such as, for example, laser beams, and sintering them. However, the results are not always satisfactory and a high outlay in terms of apparatus is required, and the problems associated with the introduction of a reduced but nevertheless high amount of energy into a complex component remain.

WO-A-03/106,051 discloses a method and an apparatus for low pressure cold spraying. In this process a coating of powder particles is sprayed in a gas substantially at ambient temperatures onto a workpiece. The process is conducted in a low ambient pressure environment which is less than atmospheric pressure to accelerate the sprayed powder particles. With this process a coating of a powder is formed on a workpiece.

EP-A-1,382,720 discloses another method and apparatus for low pressure cold spraying. In this process the target to be coated and the cold spray gun are located within a vacuum chamber at pressures below 80 kPa. With this process a workpiece is coated with a powder.

SUMMARY

An aspect of the present invention was to provide a novel process for coating substrates which is distinguished by the introduction of a small amount of energy, a low outlay in terms of apparatus and broad applicability for different carrier materials and coating materials, and wherein the metal to be applied is not melted on during processing.

An additional aspect of the present invention was the provision of a novel process for preparing dense and corrosion resistant coatings, especially tantalum coatings, which possess low content of impurities, preferably low content of oxygen and nitrogen impurities, which coatings are highly qualified for use as corrosion protective layer, especially in equipment of chemical plants.

In an embodiment, the present invention provides a cold sprayed layer of tungsten, molybdenum, titanium, zirconium, or of mixtures of two or more of tungsten, molybdenum, titanium and zirconium, or of alloys of two or more of tungsten, molybdenum, titanium and zirconium, or of alloys of tungsten, molybdenum, titanium, zirconium with other metals, wherein the cold spayed layer has an oxygen content of below 1000 ppm.

BRIEF DESCRIPTION OF THE DRAWINGS

The present invention is described in greater detail below on the basis of embodiments and of the drawings in which:

FIG. 1 shows an unetched cross-section of a tantalum coating, process gas helium;

FIG. 2 shows an unetched cross-section of a tantalum coating, process gas helium, overview picture with low magnification;

FIG. 3 shows a cross-section of a tantalum coating, etched with hydrofluoric acid, process gas helium, overview picture with low magnification;

FIG. 4 shows a cross-section of a tantalum coating, etched with hydrofluoric acid, process gas helium;

FIG. 5 shows an image section used for porosity determination, cross-section of a tantalum coating, process gas helium;

FIG. 6 shows a cross-section of a tantalum coating, etched with hydrofluoric acid, interface with the substrate, process gas helium;

FIG. 7 shows an unetched cross-section of a tantalum coating, process gas nitrogen, overview picture with low magnification;

FIG. 8 shows an unetched cross-section of a tantalum coating, process gas nitrogen;

FIG. 9 shows an image section used for porosity determination, cross-section of a tantalum coating, process gas nitrogen; and

FIG. 10 shows an unetched cross-section of a tantalum coating, process gas nitrogen, high magnification.

DETAILED DESCRIPTION

There are generally suitable for this purpose processes in which, in contrast to the conventional processes of thermal spraying (flame, plasma, high-velocity flame, arc, vacuum plasma, low-pressure plasma spraying) and of deposition-welding, there is no melting on of the coating material, caused by thermal energy produced in the coating apparatus. Contact with a flame or hot combustion gases is to be avoided, because these can cause oxidation of the powder particles and hence the oxygen content in the resulting coatings rises.

These processes are known to the person skilled in the art as, for example, cold gas spraying, cold spray processes, cold gas dynamic spraying, kinetic spraying and are described, for example, in EP-A-484533. Also suitable according to the invention is the process described in patent DE-A-10253794.

The so-called cold spray process or the kinetic spray process are particularly suitable for the method according to the invention; the cold spray process, which is described in EP-A-484533, is especially suitable, and this specification is incorporated herein by reference.

Accordingly, there is advantageously employed a method for applying coatings to surfaces, wherein a gas flow forms a gas-powder mixture with a powder of a material selected from the group consisting of niobium, tantalum, tungsten, molybdenum, titanium, zirconium, mixtures of at least two thereof or their alloys with one another or with other metals, the powder has a particle size of from 0.5 to 150 μm, wherein a supersonic speed is imparted to the gas flow and a jet of supersonic speed is formed, which ensures a speed of the powder in the gas-powder mixture of from 300 to 2000 m/s, preferably from 300 to 1200 m/s, and the jet is directed onto the surface of an object.

The metal powder particles striking the surface of the object form a coating, the particles being deformed very considerably.

The powder particles are advantageously present in the jet in an amount that ensures a flow rate density of the particles of from 0.01 to 200 g/s cm², preferably 0.01 to 100 g/s cm², very preferably 0.01 g/s cm² to 20 g/s cm², or most preferred from 0.05 g/s cm² to 17 g/s cm².

The flow rate density is calculated according to the formula F=m/(π/4*D²) where F=flow rate density, D=nozzle cross-section, m=powder feed rate. A powder feed rate of, for example, 70 g/min=1.1667 g/s is a typical example of a powder feed rate.

At low D values of below 2 mm values of markedly greater than 20 g/s cm² can be achieved. In this case F can easily assume values 50 g/s cm² or even higher at higher powder delivery rates.

As the gas with which the metal powder forms a gas-powder mixture there is generally used an inert gas such as argon, neon, helium, nitrogen or mixtures of two or more thereof. In particular cases, air may also be used. If safety regulations are met also use of hydrogen or mixtures of hydrogen with other gases can be used.

In a preferred version of the process the spraying comprises the steps of:

-   -   providing a spraying orifice adjacent a surface to be coated by         spraying;     -   providing to the spraying orifice a powder of a particulate         material chosen from the group consisting of niobium, tantalum,         tungsten, molybdenum, titanium, zirconium, mixtures of at least         two thereof or alloys thereof with one another or other metals,         the powder having a particle size of 0.5 to 150 μm, said powder         being under pressure;     -   providing an inert gas under pressure to the spraying orifice to         establish a static pressure at the spraying orifice and         providing a spray of said particulate material and gas onto the         surface to be coated; and     -   locating the spraying orifice in a region of low ambient         pressure which is less than 1 atmosphere and which is         substantially less than the static pressure at the spraying         orifice to provide substantial acceleration of the spray of said         particulate material and gas onto said surface to be coated.

In another preferred version of the process the spraying is performed with a cold spray gun and the target to be coated and the cold spray gun are located within a vacuum chamber at pressures below 80 kPa, preferably between 0.1 and 50 kPa, and most preferred between 2 and 10 kPa. Further advantageous embodiments can be found in the claims.

In general, the refractory metal has a purity of 99% or more, such as 99.5% or 99.7% or 99.9%.

According to the invention, the refractory metal advantageously has a purity of at least 99.95%, based on metallic impurities, especially of at least 99.995% or of at least 99.999%, in particular of at least 99.9995%. If an alloy is used instead of a single refractory metal, then at least the refractory metal, but preferably the alloy as a whole, has that purity, so that a corresponding highly pure coating can be produced.

In addition, the metal powder has an oxygen content of less than 1000 ppm oxygen, or less than 500, or less than 300, in particular an oxygen content of less than 100 ppm.

Particularly suitable refractory metal powders have a purity of at least 99.7%, advantageously of at least 99.9%, in particular 99.95%, and a content of less than 1000 ppm oxygen, or less than 500 ppm oxygen, or less than 300 ppm oxygen, in particular an oxygen content of less than 100 ppm.

Particularly suitable refractory metal powders have a purity of at least 99.95%, in particular of at least 99.995%, and a content of less than 1000 ppm oxygen, or less than 500 ppm oxygen, or less than 300 ppm oxygen, in particular an oxygen content of less than 100 ppm. Particularly suitable refractory metal powders have a purity of at least 99.999%, in particular of at least 99.9995%, and a content of less than 1000 ppm oxygen, or less than 500 ppm oxygen, or less than 300 ppm oxygen, in particular an oxygen content of less than 100 ppm.

In all the above-mentioned powders, the total content of other non-metallic impurities, such as carbon, nitrogen or hydrogen, should advantageously be less than 500 ppm, preferably less than 150 ppm.

In particular, the oxygen content is advantageously 50 ppm or less, the nitrogen content is 25 ppm or less and the carbon content is 25 ppm or less.

The content of metallic impurities is advantageously 500 ppm or less, preferably 100 ppm or less and most preferably 50 ppm or less, in particular 10 ppm or less.

Suitable metal powders are, for example, many of the refractory metal powders which are also suitable for the production of capacitors.

Such metal powders can be prepared by reduction of refractory metal compound with a reducing agent and preferably subsequent deoxidation. Tungsten oxide or molybdenum oxide, for example, is reduced in a stream of hydrogen at elevated temperature. The preparation is described, for example, in Schubert, Lassner, “Tungsten”, Kluwer Academic/Plenum Publishers, New York, 1999 or Brauer, “Handbuch der Praparativen Anorganischen Chemie”, Ferdinand Enke Verlag Stuttgart, 1981, p 1530.

In the case of tantalum and niobium, the preparation is in most cases carried out by reducing alkali heptafluoro-tantalates and earth alkaline metal heptafluoro-tantalates or the oxides, such as, for example, sodium heptafluorotantalate, potassium heptafluorotantalate, sodium heptafluoroniobate or potassium heptafluoroniobate, with an alkali or alkaline earth metal. The reduction can be carried out in a salt melt with the addition of, for example, sodium, or in the gas phase, calcium or magnesium vapour advantageously being used. It is also possible to mix the refractory metal compound with the alkali or alkaline earth metal and heat the mixture. A hydrogen atmosphere may be advantageous. A large number of suitable processes is known to the person skilled in the art, as are process parameters from which suitable reaction conditions can be selected. Suitable processes are described, for example, in U.S. Pat. No. 4,483,819 and WO 98/37249.

After the reduction, deoxidation is preferably carried out. This can be effected, for example, by mixing the refractory metal powder with Mg, Ca, Ba, La, Y or Ce and then heating, or by heating the refractory metal in the presence of a getter in an atmosphere that allows oxygen to pass from the metal powder to the getter. The refractory metal powder is in most cases then freed of the salts of the deoxidising agent using an acid and water, and is dried.

It is advantageous if, when using metals to lower the oxygen content, the metallic impurities can be kept low.

A further process for preparing pure powder having a low oxygen content consists in reducing a refractory metal hydride using an alkaline earth metal as reducing agent, as disclosed, for example, in WO 01/12364 and EP-A-1200218.

The thickness of the coating is usually more than 0.01 mm. Preferred are layers with a thickness between 0.05 and 10 mm, more preferred between 0.05 and 5 mm, still more preferred between 0.05 and 1 mm, still more preferred between 0.05 and 0.5 mm. The thickness may be higher as well, for example from 3 to 50 mm, or from 5 to 45 mm, or from 8 to 40 mm, or from 10 to 30 mm or from 10 to 20 mm or 10 to 15 mm.

The purities and oxygen contents of the resulting coatings should deviate not more than 50% and preferably not more than 20% from those of the powder.

Advantageously, this can be achieved by coating the substrate surface under an inert gas. Argon is advantageously used as the inert gas because, owing to its higher density than air, it tends to cover the object to be coated and to remain present, in particular when the surface to be coated is located in a vessel which prevents the argon from escaping or flowing away and more argon is continuously added.

The coatings applied according to the invention have a high purity and a low oxygen content. Advantageously, these coatings have an oxygen content of less than 1000 ppm oxygen, or less than 500, or less than 300, in particular an oxygen content of less than 100 ppm.

The coatings usually exhibit compressive stress a. Usually, the compressive stress is about −1000 MPa to 0 MPa, or from −700 MPa to 0 MPa, or from −500 MPa to 0 MPa, of from −400 MPa to 0 MPa or from −300 MPa to 0. More specifically, the compressive stress is from −200 MPa to −1000 MPa, or from −300 MPa to −700 MPa, or from −300 MPa to −500 MPa.

In general, a lower oxygen content of the powder employed will result in layers exhibiting lower compressive stress, e.g. a layer sprayed from powder having an oxygen content of 1400 ppm will usually result in a layer exhibiting compressive stress of about −970±50 MPa MPa and a layer sprayed from powder having an oxygen content of 270 ppm will usually result in a layer exhibiting compressive stress of about −460 MPa±50 MPa, more preferably −400 MPa±50 MPa.

In contrast thereto, layers produced by plasma spraying result in layers exhibiting no compressive stress at all, but tensile stress.

In particular, these coatings have a purity of at least 99.7%, advantageously of at least 99.9%, in particular of at least 99.95%, and a content of less than 1000 ppm oxygen, or less than 500 ppm oxygen, or less than 300 ppm oxygen, in particular an oxygen content of less than 100 ppm.

In particular, these coatings have a purity of at least 99.95%, in particular of at least 99.995%, and a content of less than 1000 ppm oxygen, or less than 500 ppm oxygen, or less than 300 ppm oxygen, in particular an oxygen content of less than 100 ppm.

In particular, these coatings have a purity of 99.999%, in particular of at least 99.9995%, and a content of less than 1000 ppm oxygen, or less than 500 ppm oxygen, or less than 300 ppm oxygen, in particular an oxygen content of less than 100 ppm.

The coatings according to the invention have a total content of other non-metallic impurities, such as carbon, nitrogen or hydrogen, which is advantageously below 500 ppm and most preferably below 150 ppm.

The applied coating has a content of gaseous impurities which differs by not more than 50%, or not more than 20%, or not more than 10%, or not more than 5%, or not more than 1%, from the content of the starting powder with which this coating was produced. The term “differs” is to be understood as meaning in particular an increase; the resulting coatings should, therefore, advantageously have a content of gaseous impurities that is not more than 50% greater than the content of the starting powder.

The applied coating preferably has an oxygen content which differs by not more than 5%, in particular not more than 1%, from the oxygen content of the starting powder.

The coatings according to the invention preferably have a total content of other non-metallic impurities, such as carbon, nitrogen or hydrogen, which is advantageously less than 500 ppm and most preferably less than 150 ppm. With the process of this invention layers with higher impurity contents can also be produced.

In particular, the oxygen content is advantageously 50 ppm or less, the nitrogen content is 25 ppm or less and the carbon content is 25 ppm or less.

The content of metallic impurities is advantageously 50 ppm or less, in particular 10 ppm or less.

In an advantageous embodiment, the coatings additionally have a density of at least 97%, preferably greater than 98%, in particular greater than 99% or 99.5%. 97% density of a layer means that the layer has a density of 97% of the bulk material. The density of the coating is here a measure of the closed nature and porosity of the coating. A closed, substantially pore-free coating always has a density of more than 99.5%. The density can be determined either by image analysis of a cross-sectional image (ground section) of such a coating, or alternatively by helium pycnometry. The latter method is less preferred because, in the case of very dense coatings, pores present in coatings that are more remote from the surface are not detected and a lower porosity is accordingly measured than actually exists. By means of image analysis, the density can be determined by first determining the total area of the coating to be investigated in the image area of the microscope and relating this area to the areas of the pores. In this method, pores that are located far from the surface and close to the interface with the substrate are also detected. A high density of at least 97%, preferably greater than 98%, in particular greater than 99% or 99.5%, is important in many coating processes.

The coatings show high mechanical strength which is caused by their high density and by the high deformation of the particles. In the case of tantalum, therefore, the strengths are at least 80 MPa more preferably at least 100 MPa, most preferably at least 140 MPa when nitrogen is used as the gas with which the metal powder forms a gas-powder mixture. If helium is used, the strength usually is at least 150 MPa, preferably at least 170 MPa, most preferably at least 200 MPa and very most preferred greater than 250 MPa.

Although the coatings according to the invention show high densities and low porosities, the coatings have a morphology clearly showing it was created from discrete particles. Examples can be seen, for example, in FIGS. 1 to 7. In this way the coatings according to the invention can be distinguished over coatings obtained by other methods, like coatings obtained by galvanic processes. The characteristic appearance also allows distinguishing of coatings according to the invention from coatings obtained by plasma spraying.

The articles to be coated with the process of this invention are not limited. Generally all articles which need a coating, preferably a corrosion protective coating, can be used. These articles may be made of metal and/or of ceramic material and/or of plastic material or may comprise components from these materials. Preferably surfaces of materials are coated which are subject to removal of material, for example by wear, corrosion, oxidation, etching, machining or other stress.

Preferably surfaces of materials are coated with the process of this invention which are used in corroding surroundings, for example in chemical processes in medical devices or in implants. Examples of apparatus or components to be coated are components used in chemical plants or in laboratories or in medical devices or as implants, such as reaction and mixing vessels, stirrers, blind flanges, thermowells, birsting disks, birsting disk holders, heat exchangers (shell and tubes), pipings, valves, valve bodies and pump parts.

Preferably articles are coated with the process of this invention which are no sputter targets or X-ray anodes.

The coatings prepared with the process of this invention preferably are used in corrosion protection.

The present invention therefore relates also to articles made of metal and/or of ceramic material and/or of plastic material containing at least one coatings composed of the refractory metals niobium, tantalum, tungsten, molybdenum, titanium zirconium or mixtures of two or more thereof or alloys of two or more thereof or alloys with other metals, which coatings have the above-mentioned properties.

Such coatings are in particular coatings of tantalum or niobium.

Preferably layers of tungsten, molybdenum, titanium zirconium or mixtures of two or more thereof or alloys of two or more thereof or alloys with other metals, very preferably layers of tantalum or niobium, are applied by cold spraying to the surface of a substrate to be coated. Surprisingly it has been found that with said powders or powder mixtures, preferably with tantalum and niobium powders, possessing a reduced oxygen content, for example an oxygen content below 1000 ppm, there can be produced cold sprayed layers with very high deposition rates of more than 90%. In said cold sprayed layers the oxygen content of the metal is nearly unchanged compared to the oxygen content of the powders. These cold sprayed layers show considerably higher densities than layers produced by plasma spraying or by vacuum spraying. Furthermore, these cold sprayed layers can be produced without any or with small texture, depending on powder properties and coating parameters. These cold sprayed layers are also object of this invention.

Suitable metal powders for use in the methods according to the invention are also metal powders that consist of alloys, pseudo alloys and powder mixtures of refractory metals with suitable non-refractory metals.

It is thereby possible to coat surfaces of substrates made of the same alloy or pseudo alloy.

These include especially alloys, pseudo alloys or powder mixtures of a refractory metal selected from the group consisting of niobium, tantalum, tungsten, molybdenum, titanium, zirconium or mixtures of two or more thereof, with a metal selected from the group cobalt, nickel, rhodium, palladium, platinum, copper, silver and gold. Such powders belong to the prior art, are known in principle to the person skilled in the art and are described, for example, in EP-A-774315 and EP-A-1138420.

They can be prepared by conventional processes; for example, powder mixtures are obtainable by homogenously mixing pre-prepared metal powders, it being possible for the mixing to be carried out on the one hand before use in the method according to the invention or alternatively during production of the gas-powder mixture. Alloy powders are in most cases obtainable by melting and mixing the alloying partners. According to the invention there may be used as alloy powders also so-called pre-alloyed powders. These are powders which are produced by mixing compounds such as, for example, salts, oxides and/or hydrides of the alloying partners and then reducing them, so that intimate mixtures of the metals in question are obtained. It is additionally possible according to the invention to use pseudo alloys. Pseudo alloys are understood as being materials which are obtained not by conventional melt metallurgy but, for example, by grinding, sintering or infiltration.

Known materials are, for example, tungsten/copper alloys or tungsten/copper mixtures, the properties of which are known and are listed here by way of example:

Thermal Electrical expansion Thermal Density HB conductivity coefficient conductivity Type (g/cm³) (MPa) (% IACS) (ppm/K) (W/m · K) WCu10 16.8-17.2 ≧2550 >27 6.5 170-180 WCu15 16.3 7.0 190-200 WCu20 15.2-15.6 ≧2160 >34 8.3 200-220 WCu25 14.5-15.0 ≧1940 >38 9.0 220-250 WCu30 13.8-14.4 ≧1720 >42

Also known are molybdenum-copper alloys or molybdenium/copper mixtures in the same ratios as indicated above.

Also known are molybdenum-silver alloys or molybdenium/silver mixtures which contain, for example, 10, 40 or 65 wt. % molybdenum.

Also known are tungsten-silver alloys or tungsten/silver mixtures which contain, for example, 10, 40 or 65 wt. % tungsten.

These can be used, for example, in heat pipes, cooling bodies or, in general, in temperature management systems.

It is also possible to use tungsten-rhenium alloys or mixtures, or the metal powder is an alloy having the following composition: from 94 to 99 wt. %, preferably from 95 to 97 wt. %, molybdenum, from 1 to 6 wt. %, preferably from 2 to 4 wt. %, niobium, from 0.05 to 1 wt. %, preferably from 0.05 to 0.02 wt. %, zirconium.

These alloys, like pure refractory metal powders having a purity of at least 99.95%, can be used in the recycling or production of sputter targets by means of cold gas spraying.

Suitable materials for the methods according to the invention are listed in Tables 1 to 15. Individual materials are designated with the number of the table followed by the number of the combination of components and the amount of the non-refractory metal as in Table 1. For example, material 2.005 is a material described in Table 2, the precise composition being defined with the non-refractory metal and the amount thereof as listed in Table 1, position no. 5.

Suitable niobium alloys are listed in Table 1.

TABLE 1 Amount of non- refractory metal No. Refractory metal Non-refractory metal (wt. %) 1.001 Niobium Cobalt 2-5 1.002 Niobium Nickel 2-5 1.003 Niobium Rhodium 2-5 1.004 Niobium Palladium 2-5 1.005 Niobium Platinum 2-5 1.006 Niobium Copper 2-5 1.007 Niobium Silver 2-5 1.008 Niobium Gold 2-5 1.009 Niobium Cobalt  5-10 1.010 Niobium Nickel  5-10 1.011 Niobium Rhodium  5-10 1.012 Niobium Palladium  5-10 1.013 Niobium Platinum  5-10 1.014 Niobium Copper  5-10 1.015 Niobium Silver  5-10 1.016 Niobium Gold  5-10 1.017 Niobium Cobalt 10-15 1.018 Niobium Nickel 10-15 1.019 Niobium Rhodium 10-15 1.020 Niobium Palladium 10-15 1.021 Niobium Platinum 10-15 1.022 Niobium Copper 10-15 1.023 Niobium Silver 10-15 1.024 Niobium Gold 10-15 1.025 Niobium Cobalt 15-20 1.026 Niobium Nickel 15-20 1.027 Niobium Rhodium 15-20 1.028 Niobium Palladium 15-20 1.029 Niobium Platinum 15-20 1.030 Niobium Copper 15-20 1.031 Niobium Silver 15-20 1.032 Niobium Gold 15-20 1.033 Niobium Cobalt 20-25 1.034 Niobium Nickel 20-25 1.035 Niobium Rhodium 20-25 1.036 Niobium Palladium 20-25 1.037 Niobium Platinum 20-25 1.038 Niobium Copper 20-25 1.039 Niobium Silver 20-25 1.040 Niobium Gold 20-25 1.041 Niobium Cobalt 25-30 1.042 Niobium Nickel 25-30 1.043 Niobium Rhodium 25-30 1.044 Niobium Palladium 25-30 1.045 Niobium Platinum 25-30 1.046 Niobium Copper 25-30 1.047 Niobium Silver 25-30 1.048 Niobium Gold 25-30

Table 2: Table 2 consists of 48 alloys, the refractory metal being tantalum instead of niobium and the non-refractory metal and the amount thereof in wt. % being as indicated in Table 1.

TABLE 2 Amount of non- refractory metal No. Refractory metal Non-refractory metal (wt. %) 2.001 Tantalum Cobalt 2-5 2.002 Tantalum Nickel 2-5 2.003 Tantalum Rhodium 2-5 2.004 Tantalum Palladium 2-5 2.005 Tantalum Platinum 2-5 2.006 Tantalum Copper 2-5 2.007 Tantalum Silver 2-5 2.008 Tantalum Gold 2-5 2.009 Tantalum Cobalt  5-10 2.010 Tantalum Nickel  5-10 2.011 Tantalum Rhodium  5-10 2.012 Tantalum Palladium  5-10 2.013 Tantalum Platinum  5-10 2.014 Tantalum Copper  5-10 2.015 Tantalum Silver  5-10 2.016 Tantalum Gold  5-10 2.017 Tantalum Cobalt 10-15 2.018 Tantalum Nickel 10-15 2.019 Tantalum Rhodium 10-15 2.020 Tantalum Palladium 10-15 2.021 Tantalum Platinum 10-15 2.022 Tantalum Copper 10-15 2.023 Tantalum Silver 10-15 2.024 Tantalum Gold 10-15 2.025 Tantalum Cobalt 15-20 2.026 Tantalum Nickel 15-20 2.027 Tantalum Rhodium 15-20 2.028 Tantalum Palladium 15-20 2.029 Tantalum Platinum 15-20 2.030 Tantalum Copper 15-20 2.031 Tantalum Silver 15-20 2.032 Tantalum Gold 15-20 2.033 Tantalum Cobalt 20-25 2.034 Tantalum Nickel 20-25 2.035 Tantalum Rhodium 20-25 2.036 Tantalum Palladium 20-25 2.037 Tantalum Platinum 20-25 2.038 Tantalum Copper 20-25 2.039 Tantalum Silver 20-25 2.040 Tantalum Gold 20-25 2.041 Tantalum Cobalt 25-30 2.042 Tantalum Nickel 25-30 2.043 Tantalum Rhodium 25-30 2.044 Tantalum Palladium 25-30 2.045 Tantalum Platinum 25-30 2.046 Tantalum Copper 25-30 2.047 Tantalum Silver 25-30 2.048 Tantalum Gold 25-30

Table 3: Table 3 consists of 48 alloys, the refractory metal being tungsten instead of niobium and the non-refractory metal and the amount thereof in wt. % being as indicated in Table 1.

TABLE 3 Amount of non- refractory metal No. Refractory metal Non-refractory metal (wt. %) 3.001 Tungsten Cobalt 2-5 3.002 Tungsten Nickel 2-5 3.003 Tungsten Rhodium 2-5 3.004 Tungsten Palladium 2-5 3.005 Tungsten Platinum 2-5 3.006 Tungsten Copper 2-5 3.007 Tungsten Silver 2-5 3.008 Tungsten Gold 2-5 3.009 Tungsten Cobalt  5-10 3.010 Tungsten Nickel  5-10 3.011 Tungsten Rhodium  5-10 3.012 Tungsten Palladium  5-10 3.013 Tungsten Platinum  5-10 3.014 Tungsten Copper  5-10 3.015 Tungsten Silver  5-10 3.016 Tungsten Gold  5-10 3.017 Tungsten Cobalt 10-15 3.018 Tungsten Nickel 10-15 3.019 Tungsten Rhodium 10-15 3.020 Tungsten Palladium 10-15 3.021 Tungsten Platinum 10-15 3.022 Tungsten Copper 10-15 3.023 Tungsten Silver 10-15 3.024 Tungsten Gold 10-15 3.025 Tungsten Cobalt 15-20 3.026 Tungsten Nickel 15-20 3.027 Tungsten Rhodium 15-20 3.028 Tungsten Palladium 15-20 3.029 Tungsten Platinum 15-20 3.030 Tungsten Copper 15-20 3.031 Tungsten Silver 15-20 3.032 Tungsten Gold 15-20 3.033 Tungsten Cobalt 20-25 3.034 Tungsten Nickel 20-25 3.035 Tungsten Rhodium 20-25 3.036 Tungsten Palladium 20-25 3.037 Tungsten Platinum 20-25 3.038 Tungsten Copper 20-25 3.039 Tungsten Silver 20-25 3.040 Tungsten Gold 20-25 3.041 Tungsten Cobalt 25-30 3.042 Tungsten Nickel 25-30 3.043 Tungsten Rhodium 25-30 3.044 Tungsten Palladium 25-30 3.045 Tungsten Platinum 25-30 3.046 Tungsten Copper 25-30 3.047 Tungsten Silver 25-30 3.048 Tungsten Gold 25-30

Table 4: Table 4 consists of 48 alloys, the refractory metal being molybdenum instead of niobium and the non-refractory metal and the amount thereof in wt. % being as indicated in Table 1.

TABLE 4 Amount of non- refractory metal No. Refractory metal Non-refractory metal (wt. %) 4.001 Molybdenum Cobalt 2-5 4.002 Molybdenum Nickel 2-5 4.003 Molybdenum Rhodium 2-5 4.004 Molybdenum Palladium 2-5 4.005 Molybdenum Platinum 2-5 4.006 Molybdenum Copper 2-5 4.007 Molybdenum Silver 2-5 4.008 Molybdenum Gold 2-5 4.009 Molybdenum Cobalt  5-10 4.010 Molybdenum Nickel  5-10 4.011 Molybdenum Rhodium  5-10 4.012 Molybdenum Palladium  5-10 4.013 Molybdenum Platinum  5-10 4.014 Molybdenum Copper  5-10 4.015 Molybdenum Silver  5-10 4.016 Molybdenum Gold  5-10 4.017 Molybdenum Cobalt 10-15 4.018 Molybdenum Nickel 10-15 4.019 Molybdenum Rhodium 10-15 4.020 Molybdenum Palladium 10-15 4.021 Molybdenum Platinum 10-15 4.022 Molybdenum Copper 10-15 4.023 Molybdenum Silver 10-15 4.024 Molybdenum Gold 10-15 4.025 Molybdenum Cobalt 15-20 4.026 Molybdenum Nickel 15-20 4.027 Molybdenum Rhodium 15-20 4.028 Molybdenum Palladium 15-20 4.029 Molybdenum Platinum 15-20 4.030 Molybdenum Copper 15-20 4.031 Molybdenum Silver 15-20 4.032 Molybdenum Gold 15-20 4.033 Molybdenum Cobalt 20-25 4.034 Molybdenum Nickel 20-25 4.035 Molybdenum Rhodium 20-25 4.036 Molybdenum Palladium 20-25 4.037 Molybdenum Platinum 20-25 4.038 Molybdenum Copper 20-25 4.039 Molybdenum Silver 20-25 4.040 Molybdenum Gold 20-25 4.041 Molybdenum Cobalt 25-30 4.042 Molybdenum Nickel 25-30 4.043 Molybdenum Rhodium 25-30 4.044 Molybdenum Palladium 25-30 4.045 Molybdenum Platinum 25-30 4.046 Molybdenum Copper 25-30 4.047 Molybdenum Silver 25-30 4.048 Molybdenum Gold 25-30

Table 5: Table 5 consists of 48 alloys, the refractory metal being titanium instead of niobium and the non-refractory metal and the amount thereof in wt. % being as indicated in Table 1.

TABLE 5 Amount of non- refractory metal No. Refractory metal Non-refractory metal (wt. %) 5.001 Titanium Cobalt 2-5 5.002 Titanium Nickel 2-5 5.003 Titanium Rhodium 2-5 5.004 Titanium Palladium 2-5 5.005 Titanium Platinum 2-5 5.006 Titanium Copper 2-5 5.007 Titanium Silver 2-5 5.008 Titanium Gold 2-5 5.009 Titanium Cobalt  5-10 5.010 Titanium Nickel  5-10 5.011 Titanium Rhodium  5-10 5.012 Titanium Palladium  5-10 5.013 Titanium Platinum  5-10 5.014 Titanium Copper  5-10 5.015 Titanium Silver  5-10 5.016 Titanium Gold  5-10 5.017 Titanium Cobalt 10-15 5.018 Titanium Nickel 10-15 5.019 Titanium Rhodium 10-15 5.020 Titanium Palladium 10-15 5.021 Titanium Platinum 10-15 5.022 Titanium Copper 10-15 5.023 Titanium Silver 10-15 5.024 Titanium Gold 10-15 5.025 Titanium Cobalt 15-20 5.026 Titanium Nickel 15-20 5.027 Titanium Rhodium 15-20 5.028 Titanium Palladium 15-20 5.029 Titanium Platinum 15-20 5.030 Titanium Copper 15-20 5.031 Titanium Silver 15-20 5.032 Titanium Gold 15-20 5.033 Titanium Cobalt 20-25 5.034 Titanium Nickel 20-25 5.035 Titanium Rhodium 20-25 5.036 Titanium Palladium 20-25 5.037 Titanium Platinum 20-25 5.038 Titanium Copper 20-25 5.039 Titanium Silver 20-25 5.040 Titanium Gold 20-25 5.041 Titanium Cobalt 25-30 5.042 Titanium Nickel 25-30 5.043 Titanium Rhodium 25-30 5.044 Titanium Palladium 25-30 5.045 Titanium Platinum 25-30 5.046 Titanium Copper 25-30 5.047 Titanium Silver 25-30 5.048 Titanium Gold 25-30

Table 6: Table 6 consists of 48 pseudo alloys, the refractory metal being tantalum instead of niobium and the non-refractory metal and the amount thereof in wt. % being as indicated in Table 1.

TABLE 6 Amount of non- refractory metal No. Refractory metal Non-refractory metal (wt. %) 6.001 Tantalum Cobalt 2-5 6.002 Tantalum Nickel 2-5 6.003 Tantalum Rhodium 2-5 6.004 Tantalum Palladium 2-5 6.005 Tantalum Platinum 2-5 6.006 Tantalum Copper 2-5 6.007 Tantalum Silver 2-5 6.008 Tantalum Gold 2-5 6.009 Tantalum Cobalt  5-10 6.010 Tantalum Nickel  5-10 6.011 Tantalum Rhodium  5-10 6.012 Tantalum Palladium  5-10 6.013 Tantalum Platinum  5-10 6.014 Tantalum Copper  5-10 6.015 Tantalum Silver  5-10 6.016 Tantalum Gold  5-10 6.017 Tantalum Cobalt 10-15 6.018 Tantalum Nickel 10-15 6.019 Tantalum Rhodium 10-15 6.020 Tantalum Palladium 10-15 6.021 Tantalum Platinum 10-15 6.022 Tantalum Copper 10-15 6.023 Tantalum Silver 10-15 6.024 Tantalum Gold 10-15 6.025 Tantalum Cobalt 15-20 6.026 Tantalum Nickel 15-20 6.027 Tantalum Rhodium 15-20 6.028 Tantalum Palladium 15-20 6.029 Tantalum Platinum 15-20 6.030 Tantalum Copper 15-20 6.031 Tantalum Silver 15-20 6.032 Tantalum Gold 15-20 6.033 Tantalum Cobalt 20-25 6.034 Tantalum Nickel 20-25 6.035 Tantalum Rhodium 20-25 6.036 Tantalum Palladium 20-25 6.037 Tantalum Platinum 20-25 6.038 Tantalum Copper 20-25 6.039 Tantalum Silver 20-25 6.040 Tantalum Gold 20-25 6.041 Tantalum Cobalt 25-30 6.042 Tantalum Nickel 25-30 6.043 Tantalum Rhodium 25-30 6.044 Tantalum Palladium 25-30 6.045 Tantalum Platinum 25-30 6.046 Tantalum Copper 25-30 6.047 Tantalum Silver 25-30 6.048 Tantalum Gold 25-30

Table 7: Table 7 consists of 48 pseudo alloys, the refractory metal being tungsten instead of niobium and the non-refractory metal and the amount thereof in wt. % being as indicated in Table 1.

TABLE 7 Amount of non- refractory metal No. Refractory metal Non-refractory metal (wt. %) 7.001 Tungsten Cobalt 2-5 7.002 Tungsten Nickel 2-5 7.003 Tungsten Rhodium 2-5 7.004 Tungsten Palladium 2-5 7.005 Tungsten Platinum 2-5 7.006 Tungsten Copper 2-5 7.007 Tungsten Silver 2-5 7.008 Tungsten Gold 2-5 7.009 Tungsten Cobalt  5-10 7.010 Tungsten Nickel  5-10 7.011 Tungsten Rhodium  5-10 7.012 Tungsten Palladium  5-10 7.013 Tungsten Platinum  5-10 7.014 Tungsten Copper  5-10 7.015 Tungsten Silver  5-10 7.016 Tungsten Gold  5-10 7.017 Tungsten Cobalt 10-15 7.018 Tungsten Nickel 10-15 7.019 Tungsten Rhodium 10-15 7.020 Tungsten Palladium 10-15 7.021 Tungsten Platinum 10-15 7.022 Tungsten Copper 10-15 7.023 Tungsten Silver 10-15 7.024 Tungsten Gold 10-15 7.025 Tungsten Cobalt 15-20 7.026 Tungsten Nickel 15-20 7.027 Tungsten Rhodium 15-20 7.028 Tungsten Palladium 15-20 7.029 Tungsten Platinum 15-20 7.030 Tungsten Copper 15-20 7.031 Tungsten Silver 15-20 7.032 Tungsten Gold 15-20 7.033 Tungsten Cobalt 20-25 7.034 Tungsten Nickel 20-25 7.035 Tungsten Rhodium 20-25 7.036 Tungsten Palladium 20-25 7.037 Tungsten Platinum 20-25 7.038 Tungsten Copper 20-25 7.039 Tungsten Silver 20-25 7.040 Tungsten Gold 20-25 7.041 Tungsten Cobalt 25-30 7.042 Tungsten Nickel 25-30 7.043 Tungsten Rhodium 25-30 7.044 Tungsten Palladium 25-30 7.045 Tungsten Platinum 25-30 7.046 Tungsten Copper 25-30 7.047 Tungsten Silver 25-30 7.048 Tungsten Gold 25-30

Table 8: Table 8 consists of 48 pseudo alloys, the refractory metal being molybdenum instead of niobium and the non-refractory metal and the amount thereof in wt. % being as indicated in Table 1.

TABLE 8 Amount of non- refractory metal No. Refractory metal Non-refractory metal (wt. %) 8.001 Molybdenum Cobalt 2-5 8.002 Molybdenum Nickel 2-5 8.003 Molybdenum Rhodium 2-5 8.004 Molybdenum Palladium 2-5 8.005 Molybdenum Platinum 2-5 8.006 Molybdenum Copper 2-5 8.007 Molybdenum Silver 2-5 8.008 Molybdenum Gold 2-5 8.009 Molybdenum Cobalt  5-10 8.010 Molybdenum Nickel  5-10 8.011 Molybdenum Rhodium  5-10 8.012 Molybdenum Palladium  5-10 8.013 Molybdenum Platinum  5-10 8.014 Molybdenum Copper  5-10 8.015 Molybdenum Silver  5-10 8.016 Molybdenum Gold  5-10 8.017 Molybdenum Cobalt 10-15 8.018 Molybdenum Nickel 10-15 8.019 Molybdenum Rhodium 10-15 8.020 Molybdenum Palladium 10-15 8.021 Molybdenum Platinum 10-15 8.022 Molybdenum Copper 10-15 8.023 Molybdenum Silver 10-15 8.024 Molybdenum Gold 10-15 8.025 Molybdenum Cobalt 15-20 8.026 Molybdenum Nickel 15-20 8.027 Molybdenum Rhodium 15-20 8.028 Molybdenum Palladium 15-20 8.029 Molybdenum Platinum 15-20 8.030 Molybdenum Copper 15-20 8.031 Molybdenum Silver 15-20 8.032 Molybdenum Gold 15-20 8.033 Molybdenum Cobalt 20-25 8.034 Molybdenum Nickel 20-25 8.035 Molybdenum Rhodium 20-25 8.036 Molybdenum Palladium 20-25 8.037 Molybdenum Platinum 20-25 8.038 Molybdenum Copper 20-25 8.039 Molybdenum Silver 20-25 8.040 Molybdenum Gold 20-25 8.041 Molybdenum Cobalt 25-30 8.042 Molybdenum Nickel 25-30 8.043 Molybdenum Rhodium 25-30 8.044 Molybdenum Palladium 25-30 8.045 Molybdenum Platinum 25-30 8.046 Molybdenum Copper 25-30 8.047 Molybdenum Silver 25-30 8.048 Molybdenum Gold 25-30

Table 9: Table 9 consists of 48 pseudo alloys, the refractory metal being titanium instead of niobium and the non-refractory metal and the amount thereof in wt. % being as indicated in Table 1.

TABLE 9 Amount of non- refractory metal No. Refractory metal Non-refractory metal (wt. %) 9.001 Titanium Cobalt 2-5 9.002 Titanium Nickel 2-5 9.003 Titanium Rhodium 2-5 9.004 Titanium Palladium 2-5 9.005 Titanium Platinum 2-5 9.006 Titanium Copper 2-5 9.007 Titanium Silver 2-5 9.008 Titanium Gold 2-5 9.009 Titanium Cobalt  5-10 9.010 Titanium Nickel  5-10 9.011 Titanium Rhodium  5-10 9.012 Titanium Palladium  5-10 9.013 Titanium Platinum  5-10 9.014 Titanium Copper  5-10 9.015 Titanium Silver  5-10 9.016 Titanium Gold  5-10 9.017 Titanium Cobalt 10-15 9.018 Titanium Nickel 10-15 9.019 Titanium Rhodium 10-15 9.020 Titanium Palladium 10-15 9.021 Titanium Platinum 10-15 9.022 Titanium Copper 10-15 9.023 Titanium Silver 10-15 9.024 Titanium Gold 10-15 9.025 Titanium Cobalt 15-20 9.026 Titanium Nickel 15-20 9.027 Titanium Rhodium 15-20 9.028 Titanium Palladium 15-20 9.029 Titanium Platinum 15-20 9.030 Titanium Copper 15-20 9.031 Titanium Silver 15-20 9.032 Titanium Gold 15-20 9.033 Titanium Cobalt 20-25 9.034 Titanium Nickel 20-25 9.035 Titanium Rhodium 20-25 9.036 Titanium Palladium 20-25 9.037 Titanium Platinum 20-25 9.038 Titanium Copper 20-25 9.039 Titanium Silver 20-25 9.040 Titanium Gold 20-25 9.041 Titanium Cobalt 25-30 9.042 Titanium Nickel 25-30 9.043 Titanium Rhodium 25-30 9.044 Titanium Palladium 25-30 9.045 Titanium Platinum 25-30 9.046 Titanium Copper 25-30 9.047 Titanium Silver 25-30 9.048 Titanium Gold 25-30

Table 10: Table 10 consists of 48 powder mixtures, the refractory metal being tantalum instead of niobium and the non-refractory metal and the amount thereof in wt. % being as indicated in Table 1.

TABLE 10 Amount of non- refractory metal No. Refractory metal Non-refractory metal (wt. %) 10.001 Tantalum Cobalt 2-5 10.002 Tantalum Nickel 2-5 10.003 Tantalum Rhodium 2-5 10.004 Tantalum Palladium 2-5 10.005 Tantalum Platinum 2-5 10.006 Tantalum Copper 2-5 10.007 Tantalum Silver 2-5 10.008 Tantalum Gold 2-5 10.009 Tantalum Cobalt  5-10 10.010 Tantalum Nickel  5-10 10.011 Tantalum Rhodium  5-10 10.012 Tantalum Palladium  5-10 10.013 Tantalum Platinum  5-10 10.014 Tantalum Copper  5-10 10.015 Tantalum Silver  5-10 10.016 Tantalum Gold  5-10 10.017 Tantalum Cobalt 10-15 10.018 Tantalum Nickel 10-15 10.019 Tantalum Rhodium 10-15 10.020 Tantalum Palladium 10-15 10.021 Tantalum Platinum 10-15 10.022 Tantalum Copper 10-15 10.023 Tantalum Silver 10-15 10.024 Tantalum Gold 10-15 10.025 Tantalum Cobalt 15-20 10.026 Tantalum Nickel 15-20 10.027 Tantalum Rhodium 15-20 10.028 Tantalum Palladium 15-20 10.029 Tantalum Platinum 15-20 10.030 Tantalum Copper 15-20 10.031 Tantalum Silver 15-20 10.032 Tantalum Gold 15-20 10.033 Tantalum Cobalt 20-25 10.034 Tantalum Nickel 20-25 10.035 Tantalum Rhodium 20-25 10.036 Tantalum Palladium 20-25 10.037 Tantalum Platinum 20-25 10.038 Tantalum Copper 20-25 10.039 Tantalum Silver 20-25 10.040 Tantalum Gold 20-25 10.041 Tantalum Cobalt 25-30 10.042 Tantalum Nickel 25-30 10.043 Tantalum Rhodium 25-30 10.044 Tantalum Palladium 25-30 10.045 Tantalum Platinum 25-30 10.046 Tantalum Copper 25-30 10.047 Tantalum Silver 25-30 10.048 Tantalum Gold 25-30

Table 11: Table 11 consists of 48 powder mixtures, the refractory metal being tungsten instead of niobium and the non-refractory metal and the amount thereof in wt. % being as indicated in Table 1.

TABLE 11 Amount of non- refractory metal No. Refractory metal Non-refractory metal (wt. %) 11.001 Tungsten Cobalt 2-5 11.002 Tungsten Nickel 2-5 11.003 Tungsten Rhodium 2-5 11.004 Tungsten Palladium 2-5 11.005 Tungsten Platinum 2-5 11.006 Tungsten Copper 2-5 11.007 Tungsten Silver 2-5 11.008 Tungsten Gold 2-5 11.009 Tungsten Cobalt  5-10 11.010 Tungsten Nickel  5-10 11.011 Tungsten Rhodium  5-10 11.012 Tungsten Palladium  5-10 11.013 Tungsten Platinum  5-10 11.014 Tungsten Copper  5-10 11.015 Tungsten Silver  5-10 11.016 Tungsten Gold  5-10 11.017 Tungsten Cobalt 10-15 11.018 Tungsten Nickel 10-15 11.019 Tungsten Rhodium 10-15 11.020 Tungsten Palladium 10-15 11.021 Tungsten Platinum 10-15 11.022 Tungsten Copper 10-15 11.023 Tungsten Silver 10-15 11.024 Tungsten Gold 10-15 11.025 Tungsten Cobalt 15-20 11.026 Tungsten Nickel 15-20 11.027 Tungsten Rhodium 15-20 11.028 Tungsten Palladium 15-20 11.029 Tungsten Platinum 15-20 11.030 Tungsten Copper 15-20 11.031 Tungsten Silver 15-20 11.032 Tungsten Gold 15-20 11.033 Tungsten Cobalt 20-25 11.034 Tungsten Nickel 20-25 11.035 Tungsten Rhodium 20-25 11.036 Tungsten Palladium 20-25 11.037 Tungsten Platinum 20-25 11.038 Tungsten Copper 20-25 11.039 Tungsten Silver 20-25 11.040 Tungsten Gold 20-25 11.041 Tungsten Cobalt 25-30 11.042 Tungsten Nickel 25-30 11.043 Tungsten Rhodium 25-30 11.044 Tungsten Palladium 25-30 11.045 Tungsten Platinum 25-30 11.046 Tungsten Copper 25-30 11.047 Tungsten Silver 25-30 11.048 Tungsten Gold 25-30

Table 12: Table 12 consists of 48 powder mixtures, the refractory metal being molybdenum instead of niobium and the non-refractory metal and the amount thereof in wt. % being as indicated in Table 1.

TABLE 12 Amount of non- refractory metal No. Refractory metal Non-refractory metal (wt. %) 12.001 Molybdenum Cobalt 2-5 12.002 Molybdenum Nickel 2-5 12.003 Molybdenum Rhodium 2-5 12.004 Molybdenum Palladium 2-5 12.005 Molybdenum Platinum 2-5 12.006 Molybdenum Copper 2-5 12.007 Molybdenum Silver 2-5 12.008 Molybdenum Gold 2-5 12.009 Molybdenum Cobalt  5-10 12.010 Molybdenum Nickel  5-10 12.011 Molybdenum Rhodium  5-10 12.012 Molybdenum Palladium  5-10 12.013 Molybdenum Platinum  5-10 12.014 Molybdenum Copper  5-10 12.015 Molybdenum Silver  5-10 12.016 Molybdenum Gold  5-10 12.017 Molybdenum Cobalt 10-15 12.018 Molybdenum Nickel 10-15 12.019 Molybdenum Rhodium 10-15 12.020 Molybdenum Palladium 10-15 12.021 Molybdenum Platinum 10-15 12.022 Molybdenum Copper 10-15 12.023 Molybdenum Silver 10-15 12.024 Molybdenum Gold 10-15 12.025 Molybdenum Cobalt 15-20 12.026 Molybdenum Nickel 15-20 12.027 Molybdenum Rhodium 15-20 12.028 Molybdenum Palladium 15-20 12.029 Molybdenum Platinum 15-20 12.030 Molybdenum Copper 15-20 12.031 Molybdenum Silver 15-20 12.032 Molybdenum Gold 15-20 12.033 Molybdenum Cobalt 20-25 12.034 Molybdenum Nickel 20-25 12.035 Molybdenum Rhodium 20-25 12.036 Molybdenum Palladium 20-25 12.037 Molybdenum Platinum 20-25 12.038 Molybdenum Copper 20-25 12.039 Molybdenum Silver 20-25 12.040 Molybdenum Gold 20-25 12.041 Molybdenum Cobalt 25-30 12.042 Molybdenum Nickel 25-30 12.043 Molybdenum Rhodium 25-30 12.044 Molybdenum Palladium 25-30 12.045 Molybdenum Platinum 25-30 12.046 Molybdenum Copper 25-30 12.047 Molybdenum Silver 25-30 12.048 Molybdenum Gold 25-30

Table 13: Table 13 consists of 48 powder mixtures, the refractory metal being titanium instead of niobium and the non-refractory metal and the amount thereof in wt. % being as indicated in Table 1.

TABLE 13 Amount of non- refractory metal No. Refractory metal Non-refractory metal (wt. %) 13.001 Titanium Cobalt 2-5 13.002 Titanium Nickel 2-5 13.003 Titanium Rhodium 2-5 13.004 Titanium Palladium 2-5 13.005 Titanium Platinum 2-5 13.006 Titanium Copper 2-5 13.007 Titanium Silver 2-5 13.008 Titanium Gold 2-5 13.009 Titanium Cobalt  5-10 13.010 Titanium Nickel  5-10 13.011 Titanium Rhodium  5-10 13.012 Titanium Palladium  5-10 13.013 Titanium Platinum  5-10 13.014 Titanium Copper  5-10 13.015 Titanium Silver  5-10 13.016 Titanium Gold  5-10 13.017 Titanium Cobalt 10-15 13.018 Titanium Nickel 10-15 13.019 Titanium Rhodium 10-15 13.020 Titanium Palladium 10-15 13.021 Titanium Platinum 10-15 13.022 Titanium Copper 10-15 13.023 Titanium Silver 10-15 13.024 Titanium Gold 10-15 13.025 Titanium Cobalt 15-20 13.026 Titanium Nickel 15-20 13.027 Titanium Rhodium 15-20 13.028 Titanium Palladium 15-20 13.029 Titanium Platinum 15-20 13.030 Titanium Copper 15-20 13.031 Titanium Silver 15-20 13.032 Titanium Gold 15-20 13.033 Titanium Cobalt 20-25 13.034 Titanium Nickel 20-25 13.035 Titanium Rhodium 20-25 13.036 Titanium Palladium 20-25 13.037 Titanium Platinum 20-25 13.038 Titanium Copper 20-25 13.039 Titanium Silver 20-25 13.040 Titanium Gold 20-25 13.041 Titanium Cobalt 25-30 13.042 Titanium Nickel 25-30 13.043 Titanium Rhodium 25-30 13.044 Titanium Palladium 25-30 13.045 Titanium Platinum 25-30 13.046 Titanium Copper 25-30 13.047 Titanium Silver 25-30 13.048 Titanium Gold 25-30

Table 14: Table 14 consists of 48 pseudo alloys, the refractory metal being niobium and the non-refractory metal and the amount thereof in wt. % being as indicated in Table 1.

TABLE 14 Amount of non- refractory metal No. Refractory metal Non-refractory metal (wt. %) 14.001 Niobium Cobalt 2-5 14.002 Niobium Nickel 2-5 14.003 Niobium Rhodium 2-5 14.004 Niobium Palladium 2-5 14.005 Niobium Platinum 2-5 14.006 Niobium Copper 2-5 14.007 Niobium Silver 2-5 14.008 Niobium Gold 2-5 14.009 Niobium Cobalt  5-10 14.010 Niobium Nickel  5-10 14.011 Niobium Rhodium  5-10 14.012 Niobium Palladium  5-10 14.013 Niobium Platinum  5-10 14.014 Niobium Copper  5-10 14.015 Niobium Silver  5-10 14.016 Niobium Gold  5-10 14.017 Niobium Cobalt 10-15 14.018 Niobium Nickel 10-15 14.019 Niobium Rhodium 10-15 14.020 Niobium Palladium 10-15 14.021 Niobium Platinum 10-15 14.022 Niobium Copper 10-15 14.023 Niobium Silver 10-15 14.024 Niobium Gold 10-15 14.025 Niobium Cobalt 15-20 14.026 Niobium Nickel 15-20 14.027 Niobium Rhodium 15-20 14.028 Niobium Palladium 15-20 14.029 Niobium Platinum 15-20 14.030 Niobium Copper 15-20 14.031 Niobium Silver 15-20 14.032 Niobium Gold 15-20 14.033 Niobium Cobalt 20-25 14.034 Niobium Nickel 20-25 14.035 Niobium Rhodium 20-25 14.036 Niobium Palladium 20-25 14.037 Niobium Platinum 20-25 14.038 Niobium Copper 20-25 14.039 Niobium Silver 20-25 14.040 Niobium Gold 20-25 14.041 Niobium Cobalt 25-30 14.042 Niobium Nickel 25-30 14.043 Niobium Rhodium 25-30 14.044 Niobium Palladium 25-30 14.045 Niobium Platinum 25-30 14.046 Niobium Copper 25-30 14.047 Niobium Silver 25-30 14.048 Niobium Gold 25-30

Table 15: Table 15 consists of 48 powder mixtures, the refractory metal being niobium and non-refractory metal and the amount thereof in wt. % being as indicated in Table 1.

TABLE 15 Amount of non- refractory metal No. Refractory metal Non-refractory metal (wt. %) 15.001 Niobium Cobalt 2-5 15.002 Niobium Nickel 2-5 15.003 Niobium Rhodium 2-5 15.004 Niobium Palladium 2-5 15.005 Niobium Platinum 2-5 15.006 Niobium Copper 2-5 15.007 Niobium Silver 2-5 15.008 Niobium Gold 2-5 15.009 Niobium Cobalt  5-10 15.010 Niobium Nickel  5-10 15.011 Niobium Rhodium  5-10 15.012 Niobium Palladium  5-10 15.013 Niobium Platinum  5-10 15.014 Niobium Copper  5-10 15.015 Niobium Silver  5-10 15.016 Niobium Gold  5-10 15.017 Niobium Cobalt 10-15 15.018 Niobium Nickel 10-15 15.019 Niobium Rhodium 10-15 15.020 Niobium Palladium 10-15 15.021 Niobium Platinum 10-15 15.022 Niobium Copper 10-15 15.023 Niobium Silver 10-15 15.024 Niobium Gold 10-15 15.025 Niobium Cobalt 15-20 15.026 Niobium Nickel 15-20 15.027 Niobium Rhodium 15-20 15.028 Niobium Palladium 15-20 15.029 Niobium Platinum 15-20 15.030 Niobium Copper 15-20 15.031 Niobium Silver 15-20 15.032 Niobium Gold 15-20 15.033 Niobium Cobalt 20-25 15.034 Niobium Nickel 20-25 15.035 Niobium Rhodium 20-25 15.036 Niobium Palladium 20-25 15.037 Niobium Platinum 20-25 15.038 Niobium Copper 20-25 15.039 Niobium Silver 20-25 15.040 Niobium Gold 20-25 15.041 Niobium Cobalt 25-30 15.042 Niobium Nickel 25-30 15.043 Niobium Rhodium 25-30 15.044 Niobium Palladium 25-30 15.045 Niobium Platinum 25-30 15.046 Niobium Copper 25-30 15.047 Niobium Silver 25-30 15.048 Niobium Gold 25-30

Also suitable for use in the methods according to the invention are metal powders which consist of alloys, pseudo alloys and powder mixtures of different refractory metals with one another.

For example, alloys of molybdenum and titanium in a ratio of 50:50 atomic percent or alloys of tungsten and titanium in an amount of about 90:10 wt. % are known and are suitable for use in the methods according to the invention. In principle, however, all alloys of the refractory metals with one another are suitable for use in the methods according to the invention.

Binary alloys, pseudo alloys and powder mixtures of refractory metals that are suitable for the methods according to the invention are listed in Tables 16 to 36. Individual materials are designated with the number of the table followed by the number of the combination of components as in Table 16. For example, material 22.005 is a material described in Table 22, the precise composition being defined by the refractory metals, which are listed in Table 16, position no. 5, and the amount as listed in Table 22.

No. Component 1 Component 2 16.001 Nb Ta 16.002 Nb W 16.003 Nb Mo 16.004 Nb Ti 16.005 Ta Nb 16.006 Ta W 16.007 Ta Mo 16.008 Ta Ti 16.009 W Ta 16.010 W Nb 16.011 W Mo 16.012 W Ti 16.013 Mo Ta 16.014 Mo Nb 16.015 Mo W 16.016 Mo Ti 16.017 Ti Ta 16.018 Ti Nb 16.019 Ti W 16.020 Ti Mo

Table 17: Table 17 consists of 20 alloys, pseudo alloys and powder mixtures according to Table 16, component 1 being present in an amount of 2-5 wt. %, component 2 being present in an amount ad 100 wt. % and the individual partners in the mixture being as listed in Table 16.

TABLE 17 Amount of Amount of No. Component 1 component 1 Component 2 component 2 17.001 Nb 2-5 wt. % Ta ad 100 wt. % 17.002 Nb 2-5 wt. % W ad 100 wt. % 17.003 Nb 2-5 wt. % Mo ad 100 wt. % 17.004 Nb 2-5 wt. % Ti ad 100 wt. % 17.005 Ta 2-5 wt. % Nb ad 100 wt. % 17.006 Ta 2-5 wt. % W ad 100 wt. % 17.007 Ta 2-5 wt. % Mo ad 100 wt. % 17.008 Ta 2-5 wt. % Ti ad 100 wt. % 17.009 W 2-5 wt. % Ta ad 100 wt. % 17.010 W 2-5 wt. % Nb ad 100 wt. % 17.011 W 2-5 wt. % Mo ad 100 wt. % 17.012 W 2-5 wt. % Ti ad 100 wt. % 17.013 Mo 2-5 wt. % Ta ad 100 wt. % 17.014 Mo 2-5 wt. % Nb ad 100 wt. % 17.015 Mo 2-5 wt. % W ad 100 wt. % 17.016 Mo 2-5 wt. % Ti ad 100 wt. % 17.017 Ti 2-5 wt. % Ta ad 100 wt. % 17.018 Ti 2-5 wt. % Nb ad 100 wt. % 17.019 Ti 2-5 wt. % W ad 100 wt. % 17.020 Ti 2-5 wt. % Mo ad 100 wt. %

Table 18: Table 18 consists of 20 alloys, pseudo alloys and powder mixtures according to Table 16, component 1 being present in an amount of 5-10 wt. %, component 2 being present in an amount ad 100 wt. % and the individual partners in the mixture being listed in Table 16.

TABLE 18 Amount of Amount of No. Component 1 component 1 Component 2 component 2 18.001 Nb 5-10 wt. % Ta ad 100 wt. % 18.002 Nb 5-10 wt. % W ad 100 wt. % 18.003 Nb 5-10 wt. % Mo ad 100 wt. % 18.004 Nb 5-10 wt. % Ti ad 100 wt. % 18.005 Ta 5-10 wt. % Nb ad 100 wt. % 18.006 Ta 5-10 wt. % W ad 100 wt. % 18.007 Ta 5-10 wt. % Mo ad 100 wt. % 18.008 Ta 5-10 wt. % Ti ad 100 wt. % 18.009 W 5-10 wt. % Ta ad 100 wt. % 18.010 W 5-10 wt. % Nb ad 100 wt. % 18.011 W 5-10 wt. % Mo ad 100 wt. % 18.012 W 5-10 wt. % Ti ad 100 wt. % 18.013 Mo 5-10 wt. % Ta ad 100 wt. % 18.014 Mo 5-10 wt. % Nb ad 100 wt. % 18.015 Mo 5-10 wt. % W ad 100 wt. % 18.016 Mo 5-10 wt. % Ti ad 100 wt. % 18.017 Ti 5-10 wt. % Ta ad 100 wt. % 18.018 Ti 5-10 wt. % Nb ad 100 wt. % 18.019 Ti 5-10 wt. % W ad 100 wt. % 18.020 Ti 5-10 wt. % Mo ad 100 wt. %

Table 19: Table 19 consists of 20 alloys, pseudo alloys and powder mixtures according to Table 16, component 1 being present in an amount of 10-15 wt. %, component 2 being present in an amount ad 100 wt. % and the individual partners in the mixture being as listed in Table 16.

TABLE 19 Amount of Amount of No. Component 1 component 1 Component 2 component 2 19.001 Nb 10-15 wt. % Ta ad 100 wt. % 19.002 Nb 10-15 wt. % W ad 100 wt. % 19.003 Nb 10-15 wt. % Mo ad 100 wt. % 19.004 Nb 10-15 wt. % Ti ad 100 wt. % 19.005 Ta 10-15 wt. % Nb ad 100 wt. % 19.006 Ta 10-15 wt. % W ad 100 wt. % 19.007 Ta 10-15 wt. % Mo ad 100 wt. % 19.008 Ta 10-15 wt. % Ti ad 100 wt. % 19.009 W 10-15 wt. % Ta ad 100 wt. % 19.010 W 10-15 wt. % Nb ad 100 wt. % 19.011 W 10-15 wt. % Mo ad 100 wt. % 19.012 W 10-15 wt. % Ti ad 100 wt. % 19.013 Mo 10-15 wt. % Ta ad 100 wt. % 19.014 Mo 10-15 wt. % Nb ad 100 wt. % 19.015 Mo 10-15 wt. % W ad 100 wt. % 19.016 Mo 10-15 wt. % Ti ad 100 wt. % 19.017 Ti 10-15 wt. % Ta ad 100 wt. % 19.018 Ti 10-15 wt. % Nb ad 100 wt. % 19.019 Ti 10-15 wt. % W ad 100 wt. % 19.020 Ti 10-15 wt. % Mo ad 100 wt. %

Table 20: Table 20 consists of 20 alloys, pseudo alloys and powder mixtures according to Table 16, component 1 being present in an amount of 15-20 wt. %, component 2 being present in an amount ad 100 wt. % and the individual partners in the mixture being as listed in Table 16.

TABLE 20 Amount of Amount of No. Component 1 component 1 Component 2 component 2 20.001 Nb 15-20 wt. % Ta ad 100 wt. % 20.002 Nb 15-20 wt. % W ad 100 wt. % 20.003 Nb 15-20 wt. % Mo ad 100 wt. % 20.004 Nb 15-20 wt. % Ti ad 100 wt. % 20.005 Ta 15-20 wt. % Nb ad 100 wt. % 20.006 Ta 15-20 wt. % W ad 100 wt. % 20.007 Ta 15-20 wt. % Mo ad 100 wt. % 20.008 Ta 15-20 wt. % Ti ad 100 wt. % 20.009 W 15-20 wt. % Ta ad 100 wt. % 20.010 W 15-20 wt. % Nb ad 100 wt. % 20.011 W 15-20 wt. % Mo ad 100 wt. % 20.012 W 15-20 wt. % Ti ad 100 wt. % 20.013 Mo 15-20 wt. % Ta ad 100 wt. % 20.014 Mo 15-20 wt. % Nb ad 100 wt. % 20.015 Mo 15-20 wt. % W ad 100 wt. % 20.016 Mo 15-20 wt. % Ti ad 100 wt. % 20.017 Ti 15-20 wt. % Ta ad 100 wt. % 20.018 Ti 15-20 wt. % Nb ad 100 wt. % 20.019 Ti 15-20 wt. % W ad 100 wt. % 20.020 Ti 15-20 wt. % Mo ad 100 wt. %

Table 21: Table 21 consists of 20 alloys, pseudo alloys and powder mixtures according to Table 16, component 1 being present in an amount of 20-25 wt. %, component 2 being present in an amount ad 100 wt. % and the individual partners in the mixture being as listed in Table 16.

TABLE 21 Amount of Amount of No. Component 1 component 1 Component 2 component 2 21.001 Nb 20-25 wt. % Ta ad 100 wt. % 21.002 Nb 20-25 wt. % W ad 100 wt. % 21.003 Nb 20-25 wt. % Mo ad 100 wt. % 21.004 Nb 20-25 wt. % Ti ad 100 wt. % 21.005 Ta 20-25 wt. % Nb ad 100 wt. % 21.006 Ta 20-25 wt. % W ad 100 wt. % 21.007 Ta 20-25 wt. % Mo ad 100 wt. % 21.008 Ta 20-25 wt. % Ti ad 100 wt. % 21.009 W 20-25 wt. % Ta ad 100 wt. % 21.010 W 20-25 wt. % Nb ad 100 wt. % 21.011 W 20-25 wt. % Mo ad 100 wt. % 21.012 W 20-25 wt. % Ti ad 100 wt. % 21.013 Mo 20-25 wt. % Ta ad 100 wt. % 21.014 Mo 20-25 wt. % Nb ad 100 wt. % 21.015 Mo 20-25 wt. % W ad 100 wt. % 21.016 Mo 20-25 wt. % Ti ad 100 wt. % 21.017 Ti 20-25 wt. % Ta ad 100 wt. % 21.018 Ti 20-25 wt. % Nb ad 100 wt. % 21.019 Ti 20-25 wt. % W ad 100 wt. % 21.020 Ti 20-25 wt. % Mo ad 100 wt. %

Table 22: Table 22 consists of 20 alloys, pseudo alloys and powder mixtures according to Table 16, component 1 being present in an amount of 25-30 wt. %, component 2 being present in an amount ad 100 wt. % and the individual partners in the mixture being as listed in Table 16.

TABLE 22 Amount of Amount of No. Component 1 component 1 Component 2 component 2 22.001 Nb 25-30 wt. % Ta ad 100 wt. % 22.002 Nb 25-30 wt. % W ad 100 wt. % 22.003 Nb 25-30 wt. % Mo ad 100 wt. % 22.004 Nb 25-30 wt. % Ti ad 100 wt. % 22.005 Ta 25-30 wt. % Nb ad 100 wt. % 22.006 Ta 25-30 wt. % W ad 100 wt. % 22.007 Ta 25-30 wt. % Mo ad 100 wt. % 22.008 Ta 25-30 wt. % Ti ad 100 wt. % 22.009 W 25-30 wt. % Ta ad 100 wt. % 22.010 W 25-30 wt. % Nb ad 100 wt. % 22.011 W 25-30 wt. % Mo ad 100 wt. % 22.012 W 25-30 wt. % Ti ad 100 wt. % 22.013 Mo 25-30 wt. % Ta ad 100 wt. % 22.014 Mo 25-30 wt. % Nb ad 100 wt. % 22.015 Mo 25-30 wt. % W ad 100 wt. % 22.016 Mo 25-30 wt. % Ti ad 100 wt. % 22.017 Ti 25-30 wt. % Ta ad 100 wt. % 22.018 Ti 25-30 wt. % Nb ad 100 wt. % 22.019 Ti 25-30 wt. % W ad 100 wt. % 22.020 Ti 25-30 wt. % Mo ad 100 wt. %

Table 23: Table 23 consists of 20 alloys, pseudo alloys and powder mixtures according to Table 16, component 1 being present in an amount of 30-35 wt. %, component 2 being present in an amount ad 100 wt. % and the individual partners in the mixture being as listed in Table 16.

TABLE 23 Amount of Amount of No. Component 1 component 1 Component 2 component 2 23.001 Nb 30-35 wt. % Ta ad 100 wt. % 23.002 Nb 30-35 wt. % W ad 100 wt. % 23.003 Nb 30-35 wt. % Mo ad 100 wt. % 23.004 Nb 30-35 wt. % Ti ad 100 wt. % 23.005 Ta 30-35 wt. % Nb ad 100 wt. % 23.006 Ta 30-35 wt. % W ad 100 wt. % 23.007 Ta 30-35 wt. % Mo ad 100 wt. % 23.008 Ta 30-35 wt. % Ti ad 100 wt. % 23.009 W 30-35 wt. % Ta ad 100 wt. % 23.010 W 30-35 wt. % Nb ad 100 wt. % 23.011 W 30-35 wt. % Mo ad 100 wt. % 23.012 W 30-35 wt. % Ti ad 100 wt. % 23.013 Mo 30-35 wt. % Ta ad 100 wt. % 23.014 Mo 30-35 wt. % Nb ad 100 wt. % 23.015 Mo 30-35 wt. % W ad 100 wt. % 23.016 Mo 30-35 wt. % Ti ad 100 wt. % 23.017 Ti 30-35 wt. % Ta ad 100 wt. % 23.018 Ti 30-35 wt. % Nb ad 100 wt. % 23.019 Ti 30-35 wt. % W ad 100 wt. % 23.020 Ti 30-35 wt. % Mo ad 100 wt. %

Table 24: Table 24 consists of 20 alloys, pseudo alloys and powder mixtures according to Table 16, component 1 being present in an amount of 35-40 wt. %, component 2 being present in an amount ad 100 wt. % and the individual partners in the mixture being as listed in Table 16.

TABLE 24 Amount of Amount of No. Component 1 component 1 Component 2 component 2 24.001 Nb 35-40 wt. % Ta ad 100 wt. % 24.002 Nb 35-40 wt. % W ad 100 wt. % 24.003 Nb 35-40 wt. % Mo ad 100 wt. % 24.004 Nb 35-40 wt. % Ti ad 100 wt. % 24.005 Ta 35-40 wt. % Nb ad 100 wt. % 24.006 Ta 35-40 wt. % W ad 100 wt. % 24.007 Ta 35-40 wt. % Mo ad 100 wt. % 24.008 Ta 35-40 wt. % Ti ad 100 wt. % 24.009 W 35-40 wt. % Ta ad 100 wt. % 24.010 W 35-40 wt. % Nb ad 100 wt. % 24.011 W 35-40 wt. % Mo ad 100 wt. % 24.012 W 35-40 wt. % Ti ad 100 wt. % 24.013 Mo 35-40 wt. % Ta ad 100 wt. % 24.014 Mo 35-40 wt. % Nb ad 100 wt. % 24.015 Mo 35-40 wt. % W ad 100 wt. % 24.016 Mo 35-40 wt. % Ti ad 100 wt. % 24.017 Ti 35-40 wt. % Ta ad 100 wt. % 24.018 Ti 35-40 wt. % Nb ad 100 wt. % 24.019 Ti 35-40 wt. % W ad 100 wt. % 24.020 Ti 35-40 wt. % Mo ad 100 wt. %

Table 25: Table 25 consists of 20 alloys, pseudo alloys and powder mixtures according to Table 16, component 1 being present in an amount of 40-45 wt. %, component 2 being present in an amount ad 100 wt. % and the individual partners in the mixture being as listed in Table 16.

TABLE 25 Amount of Amount of No. Component 1 component 1 Component 2 component 2 25.001 Nb 40-45 wt. % Ta ad 100 wt. % 25.002 Nb 40-45 wt. % W ad 100 wt. % 25.003 Nb 40-45 wt. % Mo ad 100 wt. % 25.004 Nb 40-45 wt. % Ti ad 100 wt. % 25.005 Ta 40-45 wt. % Nb ad 100 wt. % 25.006 Ta 40-45 wt. % W ad 100 wt. % 25.007 Ta 40-45 wt. % Mo ad 100 wt. % 25.008 Ta 40-45 wt. % Ti ad 100 wt. % 25.009 W 40-45 wt. % Ta ad 100 wt. % 25.010 W 40-45 wt. % Nb ad 100 wt. % 25.011 W 40-45 wt. % Mo ad 100 wt. % 25.012 W 40-45 wt. % Ti ad 100 wt. % 25.013 Mo 40-45 wt. % Ta ad 100 wt. % 25.014 Mo 40-45 wt. % Nb ad 100 wt. % 25.015 Mo 40-45 wt. % W ad 100 wt. % 25.016 Mo 40-45 wt. % Ti ad 100 wt. % 25.017 Ti 40-45 wt. % Ta ad 100 wt. % 25.018 Ti 40-45 wt. % Nb ad 100 wt. % 25.019 Ti 40-45 wt. % W ad 100 wt. % 25.020 Ti 40-45 wt. % Mo ad 100 wt. %

Table 26: Table 26 consists of 20 alloys, pseudo alloys and powder mixtures according to Table 16, component 1 being present in an amount of 45-50 wt. %, component 2 being present in an amount ad 100 wt. % and the individual partners in the mixture being as listed in Table 16.

TABLE 26 Amount of Amount of No. Component 1 component 1 Component 2 component 2 26.001 Nb 45-50 wt. % Ta ad 100 wt. % 26.002 Nb 45-50 wt. % W ad 100 wt. % 26.003 Nb 45-50 wt. % Mo ad 100 wt. % 26.004 Nb 45-50 wt. % Ti ad 100 wt. % 26.005 Ta 45-50 wt. % Nb ad 100 wt. % 26.006 Ta 45-50 wt. % W ad 100 wt. % 26.007 Ta 45-50 wt. % Mo ad 100 wt. % 26.008 Ta 45-50 wt. % Ti ad 100 wt. % 26.009 W 45-50 wt. % Ta ad 100 wt. % 26.010 W 45-50 wt. % Nb ad 100 wt. % 26.011 W 45-50 wt. % Mo ad 100 wt. % 26.012 W 45-50 wt. % Ti ad 100 wt. % 26.013 Mo 45-50 wt. % Ta ad 100 wt. % 26.014 Mo 45-50 wt. % Nb ad 100 wt. % 26.015 Mo 45-50 wt. % W ad 100 wt. % 26.016 Mo 45-50 wt. % Ti ad 100 wt. % 26.017 Ti 45-50 wt. % Ta ad 100 wt. % 26.018 Ti 45-50 wt. % Nb ad 100 wt. % 26.019 Ti 45-50 wt. % W ad 100 wt. % 26.020 Ti 45-50 wt. % Mo ad 100 wt. %

Table 27: Table 27 consists of 20 alloys, pseudo alloys and powder mixtures according to Table 16, component 1 being present in an amount of 50-55 wt. %, component 2 being present in an amount ad 100 wt. % and the individual partners in the mixture being as listed in Table 16.

TABLE 27 Amount of Amount of No. Component 1 component 1 Component 2 component 2 27.001 Nb 50-55 wt. % Ta ad 100 wt. % 27.002 Nb 50-55 wt. % W ad 100 wt. % 27.003 Nb 50-55 wt. % Mo ad 100 wt. % 27.004 Nb 50-55 wt. % Ti ad 100 wt. % 27.005 Ta 50-55 wt. % Nb ad 100 wt. % 27.006 Ta 50-55 wt. % W ad 100 wt. % 27.007 Ta 50-55 wt. % Mo ad 100 wt. % 27.008 Ta 50-55 wt. % Ti ad 100 wt. % 27.009 W 50-55 wt. % Ta ad 100 wt. % 27.010 W 50-55 wt. % Nb ad 100 wt. % 27.011 W 50-55 wt. % Mo ad 100 wt. % 27.012 W 50-55 wt. % Ti ad 100 wt. % 27.013 Mo 50-55 wt. % Ta ad 100 wt. % 27.014 Mo 50-55 wt. % Nb ad 100 wt. % 27.015 Mo 50-55 wt. % W ad 100 wt. % 27.016 Mo 50-55 wt. % Ti ad 100 wt. % 27.017 Ti 50-55 wt. % Ta ad 100 wt. % 27.018 Ti 50-55 wt. % Nb ad 100 wt. % 27.019 Ti 50-55 wt. % W ad 100 wt. % 27.020 Ti 50-55 wt. % Mo ad 100 wt. %

Table 28: Table 28 consists of 20 alloys, pseudo alloys and powder mixtures according to Table 16, component 1 being present in an amount of 55-60 wt. %, component 2 being present in an amount ad 100 wt. % and the individual partners in the mixture being as listed in Table 16.

TABLE 28 Amount of Amount of No. Component 1 component 1 Component 2 component 2 28.001 Nb 55-60 wt. % Ta ad 100 wt. % 28.002 Nb 55-60 wt. % W ad 100 wt. % 28.003 Nb 55-60 wt. % Mo ad 100 wt. % 28.004 Nb 55-60 wt. % Ti ad 100 wt. % 28.005 Ta 55-60 wt. % Nb ad 100 wt. % 28.006 Ta 55-60 wt. % W ad 100 wt. % 28.007 Ta 55-60 wt. % Mo ad 100 wt. % 28.008 Ta 55-60 wt. % Ti ad 100 wt. % 28.009 W 55-60 wt. % Ta ad 100 wt. % 28.010 W 55-60 wt. % Nb ad 100 wt. % 28.011 W 55-60 wt. % Mo ad 100 wt. % 28.012 W 55-60 wt. % Ti ad 100 wt. % 28.013 Mo 55-60 wt. % Ta ad 100 wt. % 28.014 Mo 55-60 wt. % Nb ad 100 wt. % 28.015 Mo 55-60 wt. % W ad 100 wt. % 28.016 Mo 55-60 wt. % Ti ad 100 wt. % 28.017 Ti 55-60 wt. % Ta ad 100 wt. % 28.018 Ti 55-60 wt. % Nb ad 100 wt. % 28.019 Ti 55-60 wt. % W ad 100 wt. % 28.020 Ti 55-60 wt. % Mo ad 100 wt. %

Table 29: Table 29 consists of 20 alloys, pseudo alloys and powder mixtures according to Table 16, component 1 being present in an amount of 60-65 wt. %, component 2 being present in an amount ad 100 wt. % and the individual partners in the mixture being as listed in Table 16.

TABLE 29 Amount of Amount of No. Component 1 component 1 Component 2 component 2 29.001 Nb 60-65 wt. % Ta ad 100 wt. % 29.002 Nb 60-65 wt. % W ad 100 wt. % 29.003 Nb 60-65 wt. % Mo ad 100 wt. % 29.004 Nb 60-65 wt. % Ti ad 100 wt. % 29.005 Ta 60-65 wt. % Nb ad 100 wt. % 29.006 Ta 60-65 wt. % W ad 100 wt. % 29.007 Ta 60-65 wt. % Mo ad 100 wt. % 29.008 Ta 60-65 wt. % Ti ad 100 wt. % 29.009 W 60-65 wt. % Ta ad 100 wt. % 29.010 W 60-65 wt. % Nb ad 100 wt. % 29.011 W 60-65 wt. % Mo ad 100 wt. % 29.012 W 60-65 wt. % Ti ad 100 wt. % 29.013 Mo 60-65 wt. % Ta ad 100 wt. % 29.014 Mo 60-65 wt. % Nb ad 100 wt. % 29.015 Mo 60-65 wt. % W ad 100 wt. % 29.016 Mo 60-65 wt. % Ti ad 100 wt. % 29.017 Ti 60-65 wt. % Ta ad 100 wt. % 29.018 Ti 60-65 wt. % Nb ad 100 wt. % 29.019 Ti 60-65 wt. % W ad 100 wt. % 29.020 Ti 60-65 wt. % Mo ad 100 wt. %

Table 30: Table 30 consists of 20 alloys, pseudo alloys and powder mixtures according to Table 16, component 1 being present in an amount of 65-70 wt. %, component 2 being present in an amount ad 100 wt. % and the individual partners in the mixture being as listed in Table 16.

TABLE 30 Amount of Amount of No. Component 1 component 1 Component 2 component 2 30.001 Nb 65-70 wt. % Ta ad 100 wt. % 30.002 Nb 65-70 wt. % W ad 100 wt. % 30.003 Nb 65-70 wt. % Mo ad 100 wt. % 30.004 Nb 65-70 wt. % Ti ad 100 wt. % 30.005 Ta 65-70 wt. % Nb ad 100 wt. % 30.006 Ta 65-70 wt. % W ad 100 wt. % 30.007 Ta 65-70 wt. % Mo ad 100 wt. % 30.008 Ta 65-70 wt. % Ti ad 100 wt. % 30.009 W 65-70 wt. % Ta ad 100 wt. % 30.010 W 65-70 wt. % Nb ad 100 wt. % 30.011 W 65-70 wt. % Mo ad 100 wt. % 30.012 W 65-70 wt. % Ti ad 100 wt. % 30.013 Mo 65-70 wt. % Ta ad 100 wt. % 30.014 Mo 65-70 wt. % Nb ad 100 wt. % 30.015 Mo 65-70 wt. % W ad 100 wt. % 30.016 Mo 65-70 wt. % Ti ad 100 wt. % 30.017 Ti 65-70 wt. % Ta ad 100 wt. % 30.018 Ti 65-70 wt. % Nb ad 100 wt. % 30.019 Ti 65-70 wt. % W ad 100 wt. % 30.020 Ti 65-70 wt. % Mo ad 100 wt. %

Table 31: Table 31 consists of 20 alloys, pseudo alloys and powder mixtures according to Table 16, component 1 being present in an amount of 70-75 wt. %, component 2 being present in an amount ad 100 wt. % and the individual partners in the mixture being as listed in Table 16.

TABLE 31 Amount of Amount of No. Component 1 component 1 Component 2 component 2 31.001 Nb 70-75 wt. % Ta ad 100 wt. % 31.002 Nb 70-75 wt. % W ad 100 wt. % 31.003 Nb 70-75 wt. % Mo ad 100 wt. % 31.004 Nb 70-75 wt. % Ti ad 100 wt. % 31.005 Ta 70-75 wt. % Nb ad 100 wt. % 31.006 Ta 70-75 wt. % W ad 100 wt. % 31.007 Ta 70-75 wt. % Mo ad 100 wt. % 31.008 Ta 70-75 wt. % Ti ad 100 wt. % 31.009 W 70-75 wt. % Ta ad 100 wt. % 31.010 W 70-75 wt. % Nb ad 100 wt. % 31.011 W 70-75 wt. % Mo ad 100 wt. % 31.012 W 70-75 wt. % Ti ad 100 wt. % 31.013 Mo 70-75 wt. % Ta ad 100 wt. % 31.014 Mo 70-75 wt. % Nb ad 100 wt. % 31.015 Mo 70-75 wt. % W ad 100 wt. % 31.016 Mo 70-75 wt. % Ti ad 100 wt. % 31.017 Ti 70-75 wt. % Ta ad 100 wt. % 31.018 Ti 70-75 wt. % Nb ad 100 wt. % 31.019 Ti 70-75 wt. % W ad 100 wt. % 31.020 Ti 70-75 wt. % Mo ad 100 wt. %

Table 32: Table 32 consists of 20 alloys, pseudo alloys and powder mixtures according to Table 16, component 1 being present in an amount of 75-80 wt. %, component 2 being present in an amount ad 100 wt. % and the individual partners in the mixture being as listed in Table 16.

TABLE 32 Amount of Amount of No. Component 1 component 1 Component 2 component 2 32.001 Nb 75-80 wt. % Ta ad 100 wt. % 32.002 Nb 75-80 wt. % W ad 100 wt. % 32.003 Nb 75-80 wt. % Mo ad 100 wt. % 32.004 Nb 75-80 wt. % Ti ad 100 wt. % 32.005 Ta 75-80 wt. % Nb ad 100 wt. % 32.006 Ta 75-80 wt. % W ad 100 wt. % 32.007 Ta 75-80 wt. % Mo ad 100 wt. % 32.008 Ta 75-80 wt. % Ti ad 100 wt. % 32.009 W 75-80 wt. % Ta ad 100 wt. % 32.010 W 75-80 wt. % Nb ad 100 wt. % 32.011 W 75-80 wt. % Mo ad 100 wt. % 32.012 W 75-80 wt. % Ti ad 100 wt. % 32.013 Mo 75-80 wt. % Ta ad 100 wt. % 32.014 Mo 75-80 wt. % Nb ad 100 wt. % 32.015 Mo 75-80 wt. % W ad 100 wt. % 32.016 Mo 75-80 wt. % Ti ad 100 wt. % 32.017 Ti 75-80 wt. % Ta ad 100 wt. % 32.018 Ti 75-80 wt. % Nb ad 100 wt. % 32.019 Ti 75-80 wt. % W ad 100 wt. % 32.020 Ti 75-80 wt. % Mo ad 100 wt. %

Table 33: Table 33 consists of 20 alloys, pseudo alloys and powder mixtures according to Table 16, component 1 being present in an amount of 80-85 wt. %, component 2 being present in an amount ad 100 wt. % and the individual partners in the mixture being as listed in Table 16.

TABLE 33 Amount of Amount of No. Component 1 component 1 Component 2 component 2 33.001 Nb 80-85 wt. % Ta ad 100 wt. % 33.002 Nb 80-85 wt. % W ad 100 wt. % 33.003 Nb 80-85 wt. % Mo ad 100 wt. % 33.004 Nb 80-85 wt. % Ti ad 100 wt. % 33.005 Ta 80-85 wt. % Nb ad 100 wt. % 33.006 Ta 80-85 wt. % W ad 100 wt. % 33.007 Ta 80-85 wt. % Mo ad 100 wt. % 33.008 Ta 80-85 wt. % Ti ad 100 wt. % 33.009 W 80-85 wt. % Ta ad 100 wt. % 33.010 W 80-85 wt. % Nb ad 100 wt. % 33.011 W 80-85 wt. % Mo ad 100 wt. % 33.012 W 80-85 wt. % Ti ad 100 wt. % 33.013 Mo 80-85 wt. % Ta ad 100 wt. % 33.014 Mo 80-85 wt. % Nb ad 100 wt. % 33.015 Mo 80-85 wt. % W ad 100 wt. % 33.016 Mo 80-85 wt. % Ti ad 100 wt. % 33.017 Ti 80-85 wt. % Ta ad 100 wt. % 33.018 Ti 80-85 wt. % Nb ad 100 wt. % 33.019 Ti 80-85 wt. % W ad 100 wt. % 33.020 Ti 80-85 wt. % Mo ad 100 wt. %

Table 34: Table 34 consists of 20 alloys, pseudo alloys and powder mixtures according to Table 16, component 1 being present in an amount of 85-90 wt. %, component 2 being present in an amount ad 100 wt. % and the individual partners in the mixture being as listed in Table 16.

TABLE 34 Amount of Amount of No. Component 1 component 1 Component 2 component 2 34.001 Nb 85-90 wt. % Ta ad 100 wt. % 34.002 Nb 85-90 wt. % W ad 100 wt. % 34.003 Nb 85-90 wt. % Mo ad 100 wt. % 34.004 Nb 85-90 wt. % Ti ad 100 wt. % 34.005 Ta 85-90 wt. % Nb ad 100 wt. % 34.006 Ta 85-90 wt. % W ad 100 wt. % 34.007 Ta 85-90 wt. % Mo ad 100 wt. % 34.008 Ta 85-90 wt. % Ti ad 100 wt. % 34.009 W 85-90 wt. % Ta ad 100 wt. % 34.010 W 85-90 wt. % Nb ad 100 wt. % 34.011 W 85-90 wt. % Mo ad 100 wt. % 34.012 W 85-90 wt. % Ti ad 100 wt. % 34.013 Mo 85-90 wt. % Ta ad 100 wt. % 34.014 Mo 85-90 wt. % Nb ad 100 wt. % 34.015 Mo 85-90 wt. % W ad 100 wt. % 34.016 Mo 85-90 wt. % Ti ad 100 wt. % 34.017 Ti 85-90 wt. % Ta ad 100 wt. % 34.018 Ti 85-90 wt. % Nb ad 100 wt. % 34.019 Ti 85-90 wt. % W ad 100 wt. % 34.020 Ti 85-90 wt. % Mo ad 100 wt. %

Table 35: Table 35 consists of 20 alloys, pseudo alloys and powder mixtures according to Table 16, component 1 being present in an amount of 90-95 wt. %, component 2 being present in an amount ad 100 wt. % and the individual partners in the mixture being as listed in Table 16.

TABLE 35 Amount of Amount of No. Component 1 component 1 Component 2 component 2 35.001 Nb 90-95 wt. % Ta ad 100 wt. % 35.002 Nb 90-95 wt. % W ad 100 wt. % 35.003 Nb 90-95 wt. % Mo ad 100 wt. % 35.004 Nb 90-95 wt. % Ti ad 100 wt. % 35.005 Ta 90-95 wt. % Nb ad 100 wt. % 35.006 Ta 90-95 wt. % W ad 100 wt. % 35.007 Ta 90-95 wt. % Mo ad 100 wt. % 35.008 Ta 90-95 wt. % Ti ad 100 wt. % 35.009 W 90-95 wt. % Ta ad 100 wt. % 35.010 W 90-95 wt. % Nb ad 100 wt. % 35.011 W 90-95 wt. % Mo ad 100 wt. % 35.012 W 90-95 wt. % Ti ad 100 wt. % 35.013 Mo 90-95 wt. % Ta ad 100 wt. % 35.014 Mo 90-95 wt. % Nb ad 100 wt. % 35.015 Mo 90-95 wt. % W ad 100 wt. % 35.016 Mo 90-95 wt. % Ti ad 100 wt. % 35.017 Ti 90-95 wt. % Ta ad 100 wt. % 35.018 Ti 90-95 wt. % Nb ad 100 wt. % 35.019 Ti 90-95 wt. % W ad 100 wt. % 35.020 Ti 90-95 wt. % Mo ad 100 wt. %

Table 36: Table 36 consists of 20 alloys, pseudo alloys and powder mixtures according to Table 16, component 1 being present in an amount of 95-99 wt. %, component 2 being present in an amount ad 100 wt. % and the individual partners in the mixture being as listed in Table 16.

TABLE 36 Amount of Amount of No. Component 1 component 1 Component 2 component 2 36.001 Nb 95-99 wt. % Ta ad 100 wt. % 36.002 Nb 95-99 wt. % W ad 100 wt. % 36.003 Nb 95-99 wt. % Mo ad 100 wt. % 36.004 Nb 95-99 wt. % Ti ad 100 wt. % 36.005 Ta 95-99 wt. % Nb ad 100 wt. % 36.006 Ta 95-99 wt. % W ad 100 wt. % 36.007 Ta 95-99 wt. % Mo ad 100 wt. % 36.008 Ta 95-99 wt. % Ti ad 100 wt. % 36.009 W 95-99 wt. % Ta ad 100 wt. % 36.010 W 95-99 wt. % Nb ad 100 wt. % 36.011 W 95-99 wt. % Mo ad 100 wt. % 36.012 W 95-99 wt. % Ti ad 100 wt. % 36.013 Mo 95-99 wt. % Ta ad 100 wt. % 36.014 Mo 95-99 wt. % Nb ad 100 wt. % 36.015 Mo 95-99 wt. % W ad 100 wt. % 36.016 Mo 95-99 wt. % Ti ad 100 wt. % 36.017 Ti 95-99 wt. % Ta ad 100 wt. % 36.018 Ti 95-99 wt. % Nb ad 100 wt. % 36.019 Ti 95-99 wt. % W ad 100 wt. % 36.020 Ti 95-99 wt. % Mo ad 100 wt. %

EXAMPLES Preparation of a Tantalum Powder

A tantalum hydride powder was mixed with 0.3 wt. % magnesium and placed in a vacuum oven. The oven was evacuated and filled with argon. The pressure was 860 Torr, a stream of argon was maintained. The oven temperature was raised to 650° C. in steps of 50° C. and, after a constant temperature had been established, was maintained for four hours. The oven temperature was then raised to 1000° C. in steps of 50° C. and, after a constant temperature had been established, was maintained for six hours. At the end of this time, the oven was switched off and cooled to room temperature under argon. Magnesium and the resulting compounds were removed in the conventional manner by acid washing. The resulting tantalum powder had a particle size of −100 mesh (<150 μm), an oxygen content of 77 ppm and a specific BET surface area of 255 cm²/g.

Preparation of a Titanium Powder

The procedure was as for the preparation of the tantalum powder. A titanium powder having an oxygen content of 93 ppm was obtained.

Preparation of a Pre-Alloyed Titanium/Tantalum Powder

A mixture of tantalum hydride powder and titanium hydride powder in a molar ratio of 1:1 was prepared and was mixed with 0.3 wt. % magnesium; the procedure as in the preparation of the tantalum powder was then followed. A titanium/tantalum powder having an oxygen content of 89 ppm was obtained.

Production of Coatings

Tantalum and niobium coatings were produced. The tantalum powder used was AMPERIT® 150.090 and the niobium powder used was AMPERIT® 160.090, both of which are commercially available materials from H.C. Starck GmbH in Goslar. The commercially available nozzle of the MOC 29 type from CGT GmbH in Ampfing was used.

Material Tantalum Tantalum Niobium Niobium Nozzle MOC 29 MOC 29 MOC 29 MOC 29 Determination of the feed rate at 0.52 Nm³/h: 3.0 rpm (g/30 s/g/min) 35.5/71.0 35.5/71.0 14.7/29.4 14.7/29.4 4.0 rpm (g/30 s/g/min) 19.8/39.6 19.8/39.6 Movement data: Spray speed/  20/333  20/333  20/333  20/333 speed of the nozzle over the substrate (m/min) (mm/s) Line feed (mm) 1.5 1.5 1.5 1.5 Spraying interval (mm) 30 30 30 30 Process gas: Nitrogen Helium Nitrogen Helium Pressure (bar) 30 28 30 28 Flow (Nm³/h) 65 190/He 60 190/He Proportion of feed gas 8 181 8 181 (%) 3 (N2) 3 (N2) Powder feed Powder feed rate (g/min) 71 71 39.6 39.6 Number of passes 3 3 3 3 Substrates 1FTa 1FS 1FTa 1FV 2FS 2FV 2FS 2FV 1FV 1FS 2FS 1RV 1RS 1RV 1RV 1RS 1RV 1RS 1RS Sheet thickness before 2.86 2.92 2.91 2.84 (mm) Sheet thickness after 3.38 3.44 3.35 3.36 (mm) Coating thickness, 520.00 520.00 436.00 524.00 approx. (μm) *) Porosity/Density 0.9%/ 2.2%/ 99.1% 97.8%

Substrates: The substrates were placed in succession on the specimen holder and coated under the indicated test conditions. The substrate description is made up as follows:

The number at the beginning indicates the number of identical substrates located next to one another. The following letter indicates whether a flat specimen (F) or a round specimen (R, tube) was used. The following letters indicate the material, Ta meaning tantalum, S meaning a structural steel, and V meaning a stainless steel (chromium-nickel steel).

Very strong and dense coatings were obtained, which exhibit low porosity and excellent adhesion to the substrates in question. The flow rate densities were between 11 and 21 g/sec*cm².

FIGS. 1 to 10 show light microscope pictures of cross-sections of the resulting tantalum coatings. No inclusions of copper or tungsten are detectable, as occurs with corresponding layers produced by vacuum plasma spraying. The porosity determination was carried out automatically by the image analysis program ImageAccess.

The present invention is not limited to embodiments described herein; reference should be had to the appended claims. 

What is claimed is:
 1. A cold sprayed layer of tungsten, molybdenum, titanium, zirconium, or of mixtures of two or more of tungsten, molybdenum, titanium and zirconium, or of alloys of two or more of tungsten, molybdenum, titanium and zirconium, or of alloys of tungsten, molybdenum, titanium, zirconium with other metals, wherein the cold spayed layer has an oxygen content of below 1,000 ppm.
 2. The cold sprayed layer as recited in claim 1, wherein the cold sprayed layer has a density of at least 97% of a density of a bulk material.
 3. The cold sprayed layer as recited in claim 1, wherein the cold sprayed layer is made of tantalum or niobium.
 4. The cold sprayed layer as recited in claim 1, wherein the cold sprayed layer is obtained by a method comprising applying coatings to surfaces, wherein a gas flow is sprayed at a supersonic speed onto a surface of an object, the gas flow comprising a mixture of a gas and a powder of a material selected from the group consisting of niobium, tantalum, tungsten, molybdenum, titanium and zirconium, alloys of nobium, tantalum, tungsten, molybdenum, titanium and zirconium, mixtures of nobium, tantalum, tungsten, molybdenum, titanium and zirconium, and alloys of nobium, tantalum, tungsten, molybdenum, titanium and zirconium with other metals, and wherein the powder has a particle size of from 0.5 to 150 μm and an oxygen content of less than 1,000 ppm.
 5. A coated object comprising at least one cold sprayed layer as recited in claim
 1. 6. The coated object as recited in claim 5, wherein the cold sprayed layer is obtained by a method comprising applying coatings to surfaces, wherein a gas flow is sprayed at a supersonic speed onto a surface of an object, the gas flow comprising a mixture of a gas and a powder of a material selected from the group consisting of niobium, tantalum, tungsten, molybdenum, titanium and zirconium, alloys of nobium, tantalum, tungsten, molybdenum, titanium and zirconium, mixtures of nobium, tantalum, tungsten, molybdenum, titanium and zirconium, and alloys of nobium, tantalum, tungsten, molybdenum, titanium and zirconium with other metals, and wherein the powder has a particle size of from 0.5 to 150 μm and an oxygen content of less than 1,000 ppm.
 7. The coated object as recited in claim 5, wherein the coated object or a component of the coated object comprises at least one of a metal, a ceramic material, and a plastic material.
 8. A process of using the coated object as recited in claim 5 as a component in at least one of a chemical plant, a laboratory, a medical device, and an implant, the process comprising: providing the coated object; and using the coated object as a component in at least one of a chemical plant, a laboratory, a medical device, and an implant.
 9. The coated object as recited in claim 5, wherein the coated object is a reaction vessel, a mixing vessel, a stirrer, a blind flange, a thermowell, a rupture disk, a rupture disk holder, a shell heat exchanger, a tube heat exchanger, a pipe, a valve, a valve body, or a part of a pump. 